Fluoroloy A08

Polymer Filled

Features and Benefits

  • Superior heat and wear resistance
  • Recommended for moderate to high speed dynamic service running against soft metals
  • Non-abrasive

Working Temperature Range

-450° to +600°F Tan
[-268° to +316°C]

Color

Tan

Typical Physical Property Values

Properties1

ASTM

Units (Metric)

Value (Metric)

Physical
Specific Gravity
 

D792

 

2.03

Mechanical
Tensile Strength
 

D4894

 

PSI [MPa]

 

3,000 [20.7]

Tensile Modulus D4894 PSI [MPa] 55,000 [379]
Elongation D4894 % 230
Compression Strength2 D695 PSI [MPa] 1,000  [6.89]
Compressive Modulus D695 PSI [MPa] 95,000  [655]
Deformation Under Load3 D621 % 8.3
Hardness D2240 Shore D 60
Coefficient of Friction Saint-Gobain .20
Thermal
Linear Coefficient of Thermal Expansion
 

E831

 

in./in./°F

7.05 x 10-5
 (78° to 392°F [26° to 200°C]) [mm/mm/°C] [12.7 x 10-5]
Mold Direction in./in./°F 7.36 x 10-5
Cross Direction [mm/mm/°C] [13.2 x 10-5]

 

1 All testing is performed at room temperature unless otherwise specified

2 Compression Strength was tested at !% strain

3 Deformation Under Load was tested at 2,000 PSI for 24 hours

Download Data Sheet

download pdf